Application: Silica refractory brick can be widely used to build all kinds of refractory linings for kilns and furnaces.
Brief Description
Silica brick adopts silica as the raw material and lime milk, iron-phosphorus and sulfite lye as the binding agent and mineralizer, are manufactured through firing in the high temperature and go through strong chemical and mechanical erosion. Silica brick is a kind of acid refractory with over 93% SiO2 content and 2.35g/cm3 true density, which has various features of low volume expansion, excellent high-temperature strength, strong acid slag erosion resistance, And the refractoriness is 1690~1710°C,RUL is beyond 1620°C.
Technical Specification Of RongSheng Silica Brick
Item | BG-94 | BG-95 | BG-96A | BG-97B | |
Chemical Composition % | SiO2 | ≥94 | ≥95 | ≥96 | ≥96 |
Fe2O3 | ≤1.5 | ≤1.5 | ≤0.8 | ≤0.7 | |
Al2O3+2(K2O+Na2O) | ≤1.0 | ≤0.5 | ≤0.7 | ||
Refractoriness ℃ | 1710 | 1710 | 1710 | 1710 | |
Apparent Porosity % | ≤22 | ≤21 | ≤21 | ≤21 | |
Bulk Density g/cm³ | ≥1.8 | ≥1.8 | ≥1.87 | ≥1.8 | |
True Density g/cm³ | ≤2.38 | ≤2.38 | ≤2.34 | ≤2.34 | |
Cold Crushing Strength Mpa | ≥24.5 | ≥29.4 | ≥35 | ≥35 | |
Refractoriness Under Load (0.2MPa)T0.6℃ | ≥1630 | ≥1650 | ≥1680 | ≥1680 | |
Permanent Linear Change On Reheating % 1500℃X2h | 0~﹢0.3 | 0~﹢0.3 | 0~﹢0.3 | 0~﹢0.3 | |
Thermal Conductivity W/m.k 1000℃ | 1.74 | 1.74 | 1.44 | 1.44 | |
20-1000℃ Thermal Expansion 10-6/℃ | 1.25 | 1.25 | 1.25 | 1.25 |